性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 190℃/2.16kg | ASTM D-1238 | 2.0 | g/10min | |
密度 |
| ASTM D-792 | 0.918 | g/cm3 | |
机械性能 | 拉伸屈服强度 |
| ASTM D-638 | 100 | kg/cm2 |
拉伸断裂强度 |
| ASTM D-638 | 260 | kg/cm2 | |
断裂伸长率 |
| ASTM D-638 | 900 | % | |
弯曲模量 |
| ASTM D-790 | 2900 | kg/cm2 | |
悬臂梁缺口冲击强度 |
| ASTM D-256 | 40 | kg.cm/cm | |
邵氏硬度 |
| ASTM D-2240 | 50 |
| |
落锤冲击强度 |
| ASTM D-1709 | 85 | g | |
拉伸断裂强度 |
| ASTM D-882 | MD | TD | MPa |
31 | 23 | ||||
断裂伸长率 |
| ASTM D-882 | MD | TD | % |
450 | 600 | ||||
拉伸模量 | 1%正割 | ASTM D-882 | MD | TD | MPa |
195 | 220 | ||||
撕裂强度 |
| ASTM D-1922 | MD | TD | g |
80 | 318 | ||||
热性能 | 维卡软化点 |
| ASTM D-1525 | 96 | ℃ |
熔点 |
| ASTM D-2117 | 121 | ℃ | |
光学性能 | 雾度 |
| ASTM D-1003 | 20 | % |
光泽度 | 45° | ASTM D-2457 | 50 |
|